Property |
ASTM Method |
Unit |
2100 10% GF |
2200 20% GF |
2300 30% GF |
2400 40% GF |
Mechanical/Physical |
Specific Gravity |
D-792 |
|
1.34 |
1.42 |
1.51 |
1.61 |
Water Absorption, 24 Hr., 23°C |
D-570 |
% |
0.21 |
0.19 |
0.16 |
0.13 |
Tensile Strength, 23°C, Type I, 0.125", Yield |
D-638 |
psi |
16,600 |
20,100 |
24,500 |
27,000 |
Elongation, 23°C, Type I, 0.125", Break |
D-638 |
% |
6 |
3 |
3 |
2.5 |
Compressive Strength, 23°C |
D-695 |
psi |
22,000 |
28,700 |
30,700 |
31,800 |
Impact Strength, 23°C, Notched Izod |
D-256 |
ft-lb/in |
1.1 |
1.6 |
2 |
2.1 |
Flexural Modulus, 23°C, 0.125" |
D-790 |
psi |
650,000 |
900,000 |
1,300,000 |
1,700,000 |
Flexural Strength, 23°C, 0.125", Break |
D-790 |
psi |
28,000 |
30,000 |
33,000 |
36,000 |
Shear Strength |
D-732 |
psi |
13,000 |
13,500 |
14,000 |
15,000 |
Rockwell Hardness, M scale |
D-785 |
M |
114 |
114 |
114 |
114 |
Thermal |
Vical Softening Temperature, Rate B |
D-1525 |
°C |
223 |
220 |
228 |
234 |
HDT, 66 psi, 0.250", unannealed |
D-648 |
°C |
210 |
210 |
212 |
216 |
HDT, 264 psi, 0.250", unannealed |
D-648 |
°C |
207 |
209 |
210 |
213 |
CTE, flow, (0-300°F) |
E-831 |
in/in/°F |
1.8X10-5 |
1.4X10-5 |
1.1X10-5 |
0.8X10-5 |
Oxygen Index (LOI) |
D-2863 |
% |
47 |
50 |
50 |
54 |
Flammability (0.25-0.41 mm thickness) |
UL 94 |
|
V-0 |
V-0 |
V-0 |
V-0 |
Electrical |
Arc Resistance, Tungsten |
D-495 |
seconds |
|
85 |
85 |
125 |
Volume Resistivity |
D-257 |
ohm-cm |
1X1017 |
7X1016 |
3X1016 |
1.5X1016 |
Dielectric Strength, in oil, 62 mils |
D-149 |
Volts/mil |
700 |
670 |
630 |
610 |
Dielectric Constant, 1 kHz |
D-150 |
|
3.5 |
3.5 |
3.7 |
3.7 |
Dissipation Factor, 1 kHz |
D-150 |
|
0.0014 |
0.0015 |
0.0015 |
0.002 |