Property
|
Method
|
Value
|
Units
|
| Physical Properties | |||
| Density | ISO 1183 | 1350 | kg/m^3 |
| Mold shrinkage - parallel | ISO 294-4 | 1.2 to 1.5 | % |
| Mold shrinkage - normal | ISO 294-4 | 1.5 to 1.8 | % |
| Water absorption (23°C-sat) | ISO 62 | 0.02 | % |
| Mechanical Properties | |||
| Tensile stress at break (5mm/min) | ISO 527-2/1A | 90 | MPa |
| Tensile strain at break (5mm/min) | ISO 527-2/1A | 8.0 | % |
| Flexural modulus (23°C) | ISO 178 | 4200 | MPa |
| Flexural strength (23°C) | ISO 178 | 145.0 | MPa |
| Unnotched impact str (Izod) @ 23°C | ISO 180/1U | 82.0 | KJ/m^2 |
| Notched impact strength (Izod) @ 23°C | ISO 180/1A | 2.6 | KJ/m^2 |
| Notched impact strength (Izod) @-30°C | ISO 180/1A | 2.5 | KJ/m^2 |
| Rockwell hardness | ISO 2039-2 | 90 | M-Scale |
| Thermal Properties | |||
| Melting temperature (10 C/min) | ISO 11357-1,-2,-3 | 280 | °C |
| Glass transition temperature (10 C/min) | ISO 11357-1,-2,-3 | 90 | °C |
| DTUL @ 1.8 MPa | ISO 75-1, -2 | 115 | °C |
| DTUL @ 8.0 MPa | ISO 75-1, -2 | 95 | °C |
| Coeff. of linear therm expansion (parallel) | ISO 11359-2 | 0.52 | E-4/°C |
| Coeff. of linear therm expansion (normal) | ISO 11359-2 | 0.53 | E-4/°C |
| thickness tested (h) | UL94 | 3.0 | mm |
| Electrical Properties | |||
| Relative permittivity - 10KHz | IEC 60250 | 2.7 | |
| Dissipation factor - 1MHz | IEC 60250 | 11 | E-4 |
| Volume resistivity | IEC 60093 | 1E9 | ohm-m |
| Electric strength | IEC 60243-1 | 18 | KV/mm |
| Comparative tracking index CTI | IEC 60112 | 125 | - |