Mechanical/Physical |
ASTM Method |
Unit |
TE-9302N |
Melt Flow Rate |
D-2116 |
g/10 min |
2.0-3.9 |
Specific Gravity |
D-792 |
|
2.12-2.17 |
Water Absorption, 24 Hr. |
D-570 |
% |
<0.01 |
Tensile Strength, 23°C |
D-1708 |
psi |
2,700-4,354 |
Ultimate Elongation, 23°C |
D-1708 |
% |
275-300 |
Compressive Strength, 23°C at 5% Strain |
D-695 |
psi |
2,200 |
Impact Strength, 23°C, Notched Izod |
D-256 |
J/m |
no break |
Flexural Modulus, 23°C |
D-790 |
psi |
95,000 |
Durometer Hardness, Shore D |
D-2240 |
D |
55 |
Coefficient of Friction |
D-1894 |
|
0 |
Deformation Under Load, 23°C, 1000 PSI, 24 Hr. |
D-621 |
% |
0.5 |
Thermal |
Melting Point |
D-3418 |
°C |
255 |
Deflection Temperature (66 PSI) |
D-648 |
°C |
160 |
Oxygen Index |
D-2863 |
% |
>95 |
Continuous Service Temperature |
|
°C |
205 |
Coefficient of Thermal Expansion (100°F to 160°F) |
D-696 |
K-1 |
5 |
Flammability |
UL 94 |
|
V-0 |
Electrical |
Surface Resistivity |
D-257 |
ohm-sq |
10-15 |
Volume Resistivity |
D-257 |
ohm-cm |
10-18 |
Dielectric Strength, short-term (10 mil film) |
D-149 |
Volts/mil |
2,000 |
Dielectric Constant, 23°C, 10 kHz Maximum |
D-150 |
|
2.15 |
Dissipation Factor, 23°C, 10 kHz, Maximum |
D-150 |
|
0.0003 |
Arc Resistance |
D-495 |
seconds |
165 |